ZC-5322 Irradiation Crosslinkable LSZH Insulation Compound for Photovotaic Cable(125℃)
ZC-5322 Irradiation Crosslinkable LSZH Insulation Compound for Photovotaic Cable(125℃)
Description
This material is used for halogen-free flame retardant(irradiation crosslinkable) wire and cable insulation material. It is made of high- quality resin, flame retardant, antioxidant agent and cross-linking agent by mixing granulation. None-halogen property makes the materials non-toxic when burning; it has excellent flame retardancy, good physical and mechanical properties and processing performance. Heat resistance level is 125℃, and it can pass the VD-1 combustion test.
Standard: TUV 2PfG 1169; UL4703; CEEIA B218
Application
- Photovoltaic system/solar panel;
- Wire and cable;
- Control wire and cable;
- Railway wire and cable
Property
|
Item |
Unit |
Test method |
Typical value |
|
|
Density@23℃ |
g/cm³ |
ASTM D792 |
≤1.3 |
|
|
Tensile strength |
MPa |
IEC 60811-1-1 |
14.5 |
|
|
Elongation at break |
% |
185 |
||
|
After aging @150℃, 168h |
Tensile strength retention |
% |
IEC 60811-1-2 |
101 |
|
Breaking elongation retention |
% |
85 |
||
|
After aging @185℃, 100h |
Tensile strength variation |
% |
IEC 60811-1-2 |
90 |
|
Breaking elongation variation |
% |
70 |
||
|
Hot prolongation@200℃, 0.2MPa, 15min |
Elongation under the load |
% |
IEC 60811-2-1 |
35-45 |
|
Permanent deformation |
% |
0 |
||
|
Low temperature bending test@-40℃, 16h |
— |
IEC 60811-1-4 |
No crack |
|
|
Combustion test |
— |
IEC 60332-1 |
VD-1 |
|
|
The halogen acid gas content |
mg/g |
IEC 60754-1 |
none |
|
|
pH |
— |
IEC 60754-2 |
5 |
|
|
Electrical conductivity |
µS/mm |
IEC 60754-2 |
3.8 |
|
|
Dielectric strength@20℃ |
MV/mm |
IEC 60243-1 |
25 |
|
|
Volume resistivity@20℃ |
Ω·cm |
ASTM D257 |
1×1015 |
|
|
Hardness |
Shore A |
ASTM D2240 |
93 |
|
|
The irradiation condition: hot prolongation(less than 45%) |
% |
— |
35-45 |
|
Processing
Recommend to use conventional single screw extruder and specific low smoke halogen-free screw.
|
Zone |
1 |
2 |
3 |
4 |
5 |
6 |
Neck |
Head |
|
Temperature Range℃ |
135 |
145 |
150 |
155 |
160 |
165 |
170 |
170 |
- Above temperature is only for reference.
Storage
- Keep at room temperature;
- Storage environment should be clean,dry and ventilated;
- Please dry it after a long-time opening;
- Best use within six months from the date of production.
Product packing
- 25kg in moisture resistant aluminum laminated bags with composite paper bags outside;
- palletized bottom.