ZC-4101 10kV Inner Semiconductive Shield Compound
ZC-4101 Inner Semiconductive Shield Compound for MV Power Cable up to 10kV
Description
This material is used for crosslinkable semiconductive wire and cable shielding material. It is made of high quality EVA resin, conductive black carbon as the main material, adding cross-linking agent, antioxidant and other additives; mixed granulation and fabrication process is stable and reliable in quality.
Application
Shielding material for 10kV crosslinkable polyethylene insulated cable conductor; Maximum working temperature is 90℃.
Property
Item |
Unit |
Test method |
Typical value |
|
Density@23℃ |
g/cm³ |
ASTM D792 |
1.12 |
|
Tensile strength |
MPa |
IEC 60811-1-1 |
16.5 |
|
Elongation at break |
% |
320 |
||
Impact embrittlement performance@-40℃ |
Failure number |
Piece |
ASTM D746 |
0/30 |
After aging @135℃, 168h |
Tensile strength variation |
% |
IEC 60811-1-2 |
+9 |
Breaking elongation variation |
% |
-3 |
||
Hot prolongation@200℃, 0.2MPa, 15min |
Elongation under the load |
% |
IEC 60811-2-1 |
48 |
Permanent deformation |
% |
-3 |
||
Volume resistivity@20℃ |
Ω·cm |
ASTM D257 |
30 |
|
Volume resistivity@90℃ |
Ω·cm |
ASTM D257 |
298 |
Processing
Recommend for polyethylene specific extruder. Draw ratio is from 18:1 to 25:1 and other equipment need to be adjusted according to the circumstance. Recommend to use 60 to 80 type wire mesh filter.
Zone |
1 |
2 |
3 |
4 |
5 |
Neck |
Head |
Die |
Temperature Range ℃ |
75 |
85 |
105 |
115 |
115 |
115 |
115 |
115 |
- Above temperature is only for reference.
Storage
- Keep at room temperature;
- Storage environment should be clean, dry and ventilated;
- Please dry it after a long-time opening.
Product packing
- 600kg in each package;
- Inner lined with plastic sealed film bag;
- Corrugated carton with tray at the bottom.