ZC-3201 Silane XLPE Compound of Sioplas Method for Wire and Cable up to 3kV
ZC-3201 Silane XLPE Compound of Sioplas Method for Wire and Cable up to 3kV
Description
This material is a kind of warm water crosslinkable polyethylene insulation compound which consisted of compound A and compound B. Compound A is made from high quality polyethylene resin, imported silane coupling agent and compound B is made from organotin catalysts and antioxidant agent. Loss-in-weight Feeder which guarantees stable precision of components. It has an excellent extrusion performance and stable physical and chemical index; Quick extruding speed and smooth surface.
Application
- Low voltage crosslinkable wire and cable insulation;
- Maximum working temperature is 90℃.
Property
|
Item |
Unit |
Test method |
Standard value |
Typical value |
|
|
Tensile strength |
MPa |
IEC 60811-1-1 |
≥13.5 |
18.0 |
|
|
Elongation at break |
% |
≥350 |
470 |
||
|
Impact embrittlement performance@-76℃ |
Failure number |
Piece |
ASTM D746 |
≤15/30 |
0/30 |
|
After aging @135℃, 168h |
Tensile strength variation |
% |
IEC 60811-1-2 |
±20 |
+6 |
|
Breaking elongation variation |
% |
±20 |
-3 |
||
|
Hot prolongation@200℃, 0.2MPa, 15min |
Elongation under the load |
% |
IEC 60811-2-1 |
≤100 |
55 |
|
Permanent deformation |
% |
≤5 |
0 |
||
|
Dielectric dissipation factor@20℃, 50HZ |
－ |
IEC 60250 |
≤0.001 |
0.0001 |
|
|
Relative dielectric constant@20℃, 50HZ |
－ |
≤2.35 |
2.25 |
||
|
Dielectric strength@20℃ |
MV/m |
IEC 60243-1 |
≥25 |
37 |
|
|
Volume resistivity@20℃ |
Ω·m |
IEC 60093 |
≥1×1014 |
6×1014 |
|
|
Gel content |
% |
ASTM D2765 |
≥60 |
66 |
|
Processing
Recommend to use polyethylene specific extruder. Draw ratio is from 18:1 to 25:1 and other equipment need to be adjusted according to the circumstance.
|
Zone |
Feeding Section |
Compression Section |
Homogenization Section |
Model Section |
|
Temperature Range ℃ |
160-180 |
180-190 |
190-200 |
195-205 |
- Above temperature is only for reference.
Storage
- Keep at room temperature;
- Storage environment should be clean, dry and ventilated;
- Best use within six months from the date of production;
- Mix compound A and B, please use it up in 8 hours;
- Compound A should be used up within 24 hours after opened.
Product packing
- 25kg in each package, of which the grafted polyethylene (compound A) is 23.75kg/bag, catalytic masterbatch material (compound B) is 1.25 kg/bag;
- Compound A and B are in moisture resistant aluminum laminated bags with composite paper bags outside;
- Palletized bottom.