ZC-3101 Peroxide XLPE Insulation Compound for MV Cable up to 10kV
ZC-3101 Peroxide XLPE Insulation Compound for MV Cable up to 10kV
Description
This material is a kind of crosslinkable polyethylene insulation compound. It is made of high quality PE resin, dicumyl peroxide agent and antioxidant agent by plasticizing granulation. Production process uses the closed system; Loss-in-weight Feeder which guarantees stable precision of components. It has stable physical and chemical index and good processing property.
Application
- 10kV crosslinkable cable insulation;
- Maximum working temperature is 90℃.
Property
|
Item |
Unit |
Test method |
Typical value |
|
|
Density@23℃ |
g/cm³ |
ASTM D792 |
0.92±0.01 |
|
|
Tensile strength |
MPa |
IEC 60811-1-1 |
23.0 |
|
|
Elongation at break |
% |
540 |
||
|
Impact embrittlement performance@-76℃ |
Failure number |
Piece |
ASTM D746 |
0/30 |
|
After aging @135℃, 168h |
Tensile strength variation |
% |
IEC 60811-1-2 |
+7 |
|
Breaking elongation variation |
% |
+1 |
||
|
Hot prolongation@200℃, 0.2MPa, 15min |
Elongation under the load |
% |
IEC 60811-2-1 |
60 |
|
Permanent deformation |
% |
0 |
||
|
Dielectric dissipation factor@20℃, 50HZ |
－ |
IEC 60250 |
1×10-4 |
|
|
Relative dielectric constant@20℃, 50HZ |
－ |
2.25 |
||
|
Dielectric strength@20℃ |
MV/m |
IEC 60243-1 |
39 |
|
|
Volume resistivity@20℃ |
Ω·m |
IEC 60093 |
8×1014 |
|
|
Gel content |
% |
ASTM D2765 |
87 |
|
Processing
Recommend to use conventional extruder (three layers co-extrusion, draw ratio is from 20:1 to 30:1) . Other equipment need to be adjusted according to the circumstance.
|
Zone |
Feeding Section |
Compression Section |
Homogenization Section |
Model Section |
|
Temperature Range℃ |
95-100 |
105-110 |
110-115 |
115-120 |
- Above temperature is only for reference.
Storage
- Keep at room temperature;
- Storage environment should be clean, dry and ventilated;
- Best use within six months from the date of production.